UiO-67
UiO-67
CAS:1072413-83-2
M.F.:C84H52O32Zr6
M.W.:2120.63
Pricing
//
Product: UIO-67
Synonyms: Zr-BPDC
CAS：1072413-83-2
Basic Information
| Unit MF. | C84H8O32Zr6 | Unit MW. | 2076.28712 | ||
| Coordination Metal | Zr | Linkers | 4,4'-biphenyl acid (CAS: 787-70-2) | ||
| Aperture | 1nm, 1.3nm | Pore volume | 1 cm3/g | ||
| Surface Area | BET Specific surface 2000 m2/g | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | Off-White Powder |  |
||
| Particle Size | particle size>1um | |||
Stability
1) UIO-67 is stable in air for weeks, and stable in aqueous for hours
2) High thermal stability, thermal decomposition temperature above 300 ° C
2) High thermal stability, thermal decomposition temperature above 300 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 3 hours at 150 degree in vacuum.
2) It is recommended to activate for 3 hours at 150 degree in vacuum.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-67 has very rigid framework, which is good carrier of catalyst.
2) UIO-67 has very rigid framework, which is good carrier of catalyst.
Characterizations
References
1）J. H. Cavka, S. Jakobsen, U. Olsbye, N. Guillou, C. Lamberti, S. Bordiga, K. P. Lillerud, J. Am. Chem. Soc. 2008, 130, 13850-13851, DOI: 10.1021/ja8057953 ; A New Zirconium Inorganic Building Brick Forming Metal Organic Frameworks with Exceptional Stability;
2) Jared B. DeCoste, Gregory W. Peterson, Himanshu Jasuja, T. Grant Glover, Yougui Huang, Krista S. Walton; Journal of Materials Chemistry A, 2013, 1, 5642-5650; DOI：10.1039/c3ta10662d; Stability and Degradation Mechanisms of Metal-Organic Frameworks containing the Zr₆O₄(OH)₄ Secondary Building Unit