CAS:2254297-29-3
M.F.:
M.W.:
Pricing
//
Product: MOF-818(Zr)
Synonyms: NA
CAS：2254297-29-3
Basic Information
| Unit MF. | C24H24N12O44Cu6Zr6 | Unit MW. | 2132.49 | ||
| Coordination Metal | Zr , Cu | Linkers | H2PyC（CAS：37718-11-9） | ||
| Aperture | 3.7nm | Pore volume | 1 cm3/g | ||
| Surface Area | BET Specific surface >2000 m2/g, | ||||
| Analog Structure | |||||
Product Property
| Appearance | Light Blue Powder |  |
||
| Particle Size | ||||
Stability
1) MOF-818 is stable in air, stable for days in aqueous and acidic conditions(stable in PH 1-12)
2) High thermal stability, thermal decomposition temperature above 400 ° C
2) High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to degass for 6 hours at 120 degree in vacuum before gas adsorption test.
2) It is recommended to degass for 6 hours at 120 degree in vacuum before gas adsorption test.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) With pore size above 3.5nm, MOF-818 is promising in encapsulating enzyme and peptide
2) With pore size above 3.5nm, MOF-818 is promising in encapsulating enzyme and peptide
Characterizations
References
1) Qi Liu, Yinyin Song, Yanhang Ma, Yi Zhou, Hengjiang Cong, Chao Wang, Jorryn Wu, Gaoli Hu, Michael O’Keeffe, Hexiang Deng*. J. Am. Chem. Soc. 2019, 141, 1, 488-496, DOI: 10.1021/acs.chemmater.8b03216 ; Mesoporous Cages in Chemically Robust MOFs Created by a Large Number of Vertices with Reduced Connectivity