UiO-66
CAS:
M.F.:C48H28O32Zr6
M.W.:1664.06
Pricing
//
Product: UIO-66 nanoparticles
Synonyms: NA
CAS：1072413-89-8
Basic Information
| Unit MF. | C48H24O32Zr6 | Unit MW. | 1660.03 | ||
| Coordination Metal | Zr | Linkers | Terephthalic acid (CAS: 100-21-0) | ||
| Pore Size | 0.8nm; 1.1nm | Pore volume | 0.5 cm3/g | ||
| Surface Area | BET Specific surface >800 m2/g, | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | White Powder |  |
||
| Particle Size | 200nm-1um | |||
Stability
1) UIO-66 is stable in air, stable in aqueous and acidic conditions(stable in PH 1-12)
2）High thermal stability, thermal decomposition temperature above 400 ° C
2）High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to degas for 12 hours at 120 degree in vacuum before gas-adsorption test.
2) It is recommended to degas for 12 hours at 120 degree in vacuum before gas-adsorption test.
3) Ultrasonic despersion in methanol/ethanol/DMF before in-vitro test
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-66 has very rigid framework, which is good carrier of catalyst.
2) UIO-66 has very rigid framework, which is good carrier of catalyst.
Characterizations
References
1) J. H. Cavka, S. Jakobsen, U. Olsbye, N. Guillou, C. Lamberti, S. Bordiga, K. P. Lillerud, J. Am. Chem. Soc. 2008, 130, 13850-13851, DOI: 10.1021/ja8057953 ; A New Zirconium Inorganic Building Brick Forming Metal Organic Frameworks with Exceptional Stability
2) S. J. Garibaya, S. M. Cohen, Chem. Commun., 2010,46, 7700-7702, DOI: 10.1039/C0CC02990D ; Isoreticular synthesis and modification of frameworks with the UiO-66 topology
3) P.Yang, F. Mao, Y. Li, Q. Zhuang, J. Gu, Chem. Eur. J. 2018, 24, 2962-2970, DOI : 10.1002/chem.201705020 ; Hierarchical Porous Zr‐Based MOFs Synthesized by a Facile Monocarboxylic Acid Etching Strategy