UIO-66-F
UIO-66-F
CAS:1380595-28-7
M.F.:
M.W.:
Pricing
//
Product: UIO-66-F
Synonyms: F-UIO-66(Zr); Fluorinated-UIO-66(Zr);
CAS：1380595-28-7
Basic Information
| Unit MF. | C48F624O32Zr6 | Unit MW. | 1749.83 | ||
| Coordination Metal | Zr | Linkers | 2-fluoroterephthalic acid (CAS: 3906-87-4) | ||
| Pore Size | 0.8nm; 1.1nm | Pore volume | 0.5 cm3/g | ||
| Surface Area | BET Specific surface >700 m2/g, | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | White Powder | |||
| Particle Size | um scale irregular particles | |||
Stability
1) UIO-66-F is stable in air, stable in aqueous and acidic conditions(stable in PH 1-12)
2) High thermal stability, thermal decomposition temperature above 400 ° C
2) High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 12 hours at 120 degree in vacuum.
2) It is recommended to activate for 12 hours at 120 degree in vacuum.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-66-F4 has very rigid framework, which is good carrier of catalyst
2) UIO-66-F4 has very rigid framework, which is good carrier of catalyst
Characterizations
References
1）Zhigang Hu, Yongwu Peng, Zixi Kang, Yuhong Qian, Dan Zhao, Inorg. Chem. 2015, 54, 4862-4868, DOI: 10.1021/acs.inorgchem.5b00435 ; A Modulated Hydrothermal (MHT) Approach for the Facile Synthesis
of UiO-66-Type MOFs