UIO-66-NO2
UIO-66-NO2
CAS:1260119-01-4
M.F.:C48H22N6O44Zr6
M.W.:1934.05
Pricing
//
Product: NO2-UIO-66
Synonyms: UIO-66-NO2
CAS：1260119-01-4
Basic Information
| Unit MF. | C48H18N6O44Zr6 | Unit MW. | 1930.01 | ||
| Coordination Metal | Zr | Linkers | Nitroterephthalic acid (CAS: 610-29-7) | ||
| Pore Size | 0.8nm; 1.1nm | Pore volume | 0.5 cm3/g | ||
| Surface Area | BET Specific surface 600-800 m2/g, | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | White Powder | |||
| Particle Size | <100nm nanoparticles | |||
Stability
1) NO2-UIO-66 is stable in air and aqueous conditions(stable in PH 1-13)
2) High thermal stability, thermal decomposition temperature above 400 ° C
2) High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 3 hours at 150 degree in vacuum.
2) It is recommended to activate for 3 hours at 150 degree in vacuum.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-66 has very rigid framework, which is good carrier of catalyst.
2) UIO-66 has very rigid framework, which is good carrier of catalyst.
Characterizations
References
1) F. Vermoortele,M. Vandichel, B. Van de Voorde, R. Ameloot, M. Waroquier, V. Van Speybroeck, D. E. De Vos, Angew. Chem., Int. Ed. 2012, 51(20), 4887-4890, DOI: 10.1002/anie.201108565 ; Electronic Effects of Linker Substitution on Lewis Acid Catalysis with Metal–Organic Frameworks